达森特焊接材料(苏州)有限公司

备注:一口价为一公斤价格;

OK Autrod 4047铝硅焊丝

品牌:瑞典伊萨

铝焊丝标准:GB/T1  AWS A5.10

焊丝直径:0.9、1.0、1.2、1.6、2.0、2.4、3.0、3.2、4.0、5.0(mm)

焊丝盘尺寸:D300(9kg)、D270(7kg)、D200(2kg)、D100(0.5kg)

包装状态:盘丝、直条

焊丝特点:12%硅含量,流动性好,焊接温度低。

推荐焊接方法:钎焊(俗称:氧气焊、火焰焊),配201铝焊粉。

焊接应用:焊接以下铝合金汽车铝水箱、中冷器、散热器、铝合金客车窗、自行车车架、铝件维修。                                                                      

OK Autrod 4047

GMAW

OK Autrod 4047 was originally developed as a brazing alloy to take advantage of its low melting point and narrow freezing range. In addition, it has a higher silicon content than OK Autrod 4043, which provides increased fluidity and reduced shrinkage. The alloy produces bright, almost smut-free welds. Hot cracking is significantly reduced when using OK Autrod 4047 as a filler alloy. The alloy can be used in applications with sustained elevated temperatures. Non-heat treatable.

Welding current

DC(+)

Classifications Approvals Typical all weld metal composition, %Typical mech. properties all weld metal

SFA/AWS A5.10

ER4047

EN ISO 18273

S Al 4047 (AlSi12)

CWB AWS A5.10 (Item number ending with A)

       Si 12,0     Mn <0,15     Cu <0,05     Ti <0,15     Zn <0,20      Fe <0,6

Wire composition

Yield stress, MPa      Tensile strength, MPa     Elongation, %      Elongation, %

        80                      170                   12                  12

Diameter, mm                        0,9          1,2           1,6

Arc voltage, V                     13-24        20-29         25-30

Welding current, A                 60-170      140-260       190-350

Wire feed, m/min                     -           6-13        4,5-7,5

Deposition rate kg weld metal/hour - 1,1-2,4 1,5-2,5